ชื่อเรื่อง: Preparation of Ferroelectric KNbO3 Based Borate Glass System
ผู้แต่ง/ผู้ร่วมงาน: Kruea-In, Chatchai
Intawin, Pratthana
Leenakul, Wilaiwan
คำสำคัญ: Transparent Glass
Dielectric
Microstructure
วันที่เผยแพร่: 2015
สำนักพิมพ์: Journal of Nanoscience and Nanotechnology
บทคัดย่อ: The incorporation method was employed to produce ferroelectric glass ceramics from the K2O–Nb2O5–B2O3 glass system. The nanocrystalline potassium niobate (KNbO3) was first prepared using a simple mixed oxide method, where the B2O3 was initially mixed and then melted to form glass. The successfully produced optically transparent glass was then subjected to a heat treatment schedule for further crystallization at temperatures ranging from 500 to 650 C, which resulted in the precipitation of the KNbO3 phase, together with the K3B2Nb3O12 phase. Scanning electron microscopy (SEM) showed the presence of randomly oriented KNbO3 crystals dispersed in a continuous glass matrix. It was found that the glass ceramics subjected to the heat treatment at temperatures higher than 545 C were opaque, while the lower gave a highly transparent glass ceramics. The crystal size and crystallinity were found to increase with increasing heat treatment temperature, which in turn plays an important role in controlling the properties of the glass ceramics,including physical, optical, and dielectric properties.
URI: http://cmruir.cmru.ac.th/handle/123456789/1491
ปรากฏในกลุ่มข้อมูล:Article

แฟ้มในรายการข้อมูลนี้:
ไม่มีแฟ้มใดที่สัมพันธ์กับรายการข้อมูลนี้


รายการทั้งหมดในระบบคิดีได้รับการคุ้มครองลิขสิทธิ์ มีการสงวนสิทธิ์เว้นแต่ที่ระบุไว้เป็นอื่น